Structural, Optical and Electrochromic Properties of WO3 Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique
Guang Pu Xue Yu Guang Pu Fen Xi/Spectroscopy and Spectral Analysis, cilt.38, sa.9, ss.2982-2988, 2018 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 38 Sayı: 9
- Basım Tarihi: 2018
- Doi Numarası: 10.3964/j.issn.1000-0593(2018)09-2982-07
- Dergi Adı: Guang Pu Xue Yu Guang Pu Fen Xi/Spectroscopy and Spectral Analysis
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.2982-2988
- Anahtar Kelimeler: Spin coating, Spray pyrolysis, WO3
- Erzincan Binali Yıldırım Üniversitesi Adresli: Evet
Özet
© 2018, Peking University Press. All right reserved.In this study, Tungsten Oxide (WO3) thin films were prepared by Chemical Spray Pyrolysis (CSP) and Spin Coating (SC) techniques and it was investigated effects of technique and parameter on the films. WO3 thin films were deposited on ITO (Indium Tin Oxide) coated glasses. The structural, optical and electrochromic properties of the WO3 thin films were characterized by XRD, SEM, UV, and CV measurements. The sharpest (200) peak was observed in the XRD spectra and optical band gaps were calculated around 2.6~3.1 eV via UV-Vis spectra for all of the samples. Micro fibrous reticulated surface (filamentous like) morphology for the films deposited by CSP technique and smooth surface morphology with high optical transmittance for the film deposited by SC Technique were obtained from SEM images. In addition to these results, it was revealed that all the samples exhibit good electrochromic performance.